Formation of weld crater in GMAW of aluminum alloys. (English) Zbl 1179.80022
Summary: Both mathematical modeling and experiments have been conducted on the formation of the crater formed in a gas metal arc welding (GMAW) of aluminum alloy 6005-T4. Transient weld pool shape and the distributions of temperature and velocity were calculated by a three-dimensional numerical model. The final weld bead shape and dimensions were obtained. Corresponding experiments were conducted and in good agreement with modeling predictions. Metallurgical characterizations were also performed on the experimental samples. It was found that due to the fast solidification of the weld pool after the termination of the welding arc, there is no time for the molten metal to flow back towards the weld pool center and close up the crater. Thus a crater was formed at the end of the weld bead. Solidification cracking was formed at the center of weld crater. A “back-up” technique was proposed to allow extra molten metal to flow back to the crater and fill it up. The crater was successfully filled and the crater cracking was eliminated.
MSC:
80A20 Heat and mass transfer, heat flow (MSC2010)
76T99 Multiphase and multicomponent flows
76-05 Experimental work for problems pertaining to fluid mechanics
80-05 Experimental work for problems pertaining to classical thermodynamics
76M25 Other numerical methods (fluid mechanics) (MSC2010)
PDF BibTeX XML Cite
Full Text: DOI
References:
[1] H.L. Saunders, Welding Aluminum: Theory and Practice, 3rd ed., The Aluminum Association, 1997, pp. 1.2 – 9.5.
[2] Dickerson, P. B.: Weld discontinuities – causes and cures, Weld. J. 77, No. 6, 37-42 (1998)
[3] P. Dickerson, Quality control in aluminum arc welding, in: Proceedings of the Aluminum Joining Seminar Aluminum Association, Washington, DC, Landmark Motor Hotel, Metarie, Louisiana, 1986, pp. 331 – 359.
[4] Runnerstam, O.; Persson, K.: The importance of a good quality gas shield, Svetsaren 50, No. 3, 24-27 (1995)
[5] Pereira, M.; Taniguchi, C.; Brandi, S.; Machida, S.: Analysis of solidification cracks in welds of al – mg – si A6351 type alloy welded by high frequency pulsed TIG process, Q. J. Jpn. weld. Soc. 12, No. 3, 342-350 (1994)
[6] Kerr, H.; Katoh, M.: Investigation of heat-affected zone cracking of GMA welds of al – mg – si alloys using the varestraint test, Weld. J. 66, No. 9, 251s-259s (1987)
[7] Lu, Z.; Evans, W.; Praker, J.; Birley, S.: Simulation of microstructure and liquation cracking in 7017 aluminum alloy, Mater. sci. Eng. A 220, 1-7 (1996)
[8] M. Mizuno, S. Takeno, T. Teramoto, Y. Sakei, Relations between restraint intensity and weld cracking in welding of aluminium alloy, in: Proceedings of the Third International Conference Aluminium-Verlag, Duesseldorf, Munich, FRG, 1985, pp. I.5.1 – I.5.13.
[9] E.C. Partington, Control of metal transfer in modulated pulse M.I.G. welding, in: IIW Asian Pacific Regional Welding Congress, 1988, pp. 970 – 988.
[10] Sunwoo, A. J.; Iii, E. L. Bradley; Jr., J. W. Morris: Effects of heat-affected zone peak temperature on the microstructure and properties of 2090 al alloy, Metall. trans. A 21A, No. 10, 2795-2804 (1990)
[11] Guittnerez, L. A.; Neye, G.; Zschech, E.: Microstructure, hardness profile and tensile strength in welds of AA6013 T6 extrusions, Weld. J. 75, No. 4, 115s-121s (1996)
[12] Lu, M. J.; Kou, S.: Power inputs in gas metal arc welding of aluminum – part 1, Weld. J. 68, No. 9, 382s-388s (1989)
[13] Kluken, A. O.; Bjorneklett, B.: A study of mechanical properties for aluminum GMA weldments, Weld. J. 76, No. 2, 39-44 (1997)
[14] Ma, T.; Ouden, G.: Heat-affected zone softening during arc welding of al – zn – mg alloys, Int. J. Join. mater. 8, No. 3, 105-110 (1996)
[15] Martukanitz, R. P.; Natalie, C. A.; Knoefel, J. O.: The weldability of an al – Li – cu alloy, J. met. 39, No. 11, 38-42 (1987)
[16] Budnik, V. P.: Effect of the type of inert gas on pool temperature and fracture of the oxide film in welding aluminium, Paton weld. J. 6, No. 12, 23-25 (1994)
[17] Domey, J.; Aidun, D. K.; Ahmadi, G.; Regel, L. L.; Wilcox, W. R.: Numerical simulation of the effect of gravity on weld pool shape, Weld. J. 74, No. 8, 263s-268s (1995)
[18] Kim, W. H.; Fan, H. G.; Na, S. J.: Effect of various driving forces on heat and mass transfer in arc welding, Numer. heat transfer A 32, 633-652 (1997)
[19] Hong, K.; Weckman, D. C.; Strong, A. B.: The influence of thermofluids phenomena in gas tungsten arc welds in high and low thermal conductivity metals, Can. metall. Q. 37, No. 3 – 4, 303-393 (1998)
[20] Wang, Y.; Shi, Q.; Tsai, H. L.: Modeling of the effects of surface-active elements on flow patterns and weld penetration, Metall. mater. Trans. B 32B, No. 2, 145-161 (2001)
[21] Choo, R. T. C.; Szekely, J.; Westhoff, R. C.: On the calculation of the free surface temperature of gas-tungsten-arc weld pools from first principles. Part I. Modeling the weld arc, Metall. trans. B 23B, No. 6, 357-369 (1992)
[22] Choo, R. T. C.; Szekely, J.; David, S. A.: On the calculation of the free surface temperature of gas-tungsten-arc weld pools from first principles. Part II. Modeling the weld pool and comparison with experiments, Metall. trans. B 23B, No. 6, 371-384 (1992)
[23] Wang, Y.; Tsai, H. L.: Impingement of filler droplets and weld pool dynamics during gas metal arc welding process, Int. J. Heat mass transfer 44, 2067-2080 (2001) · Zbl 1064.76624 · doi:10.1016/S0017-9310(00)00251-9
[24] Lee, S. -Y.; Na, S. -J.: A numerical analysis of a stationary gas tungsten welding arc considering various electrode angles, Weld. J. 75, No. 9, 259s-269s (1996)
[25] Ushio, M.; Wu, C. S.: Mathematical modeling of three-dimensional heat and fluid flow in a moving gas metal arc weld pool, Metall. mater. Trans. B 28B, No. 6, 509-516 (1995)
[26] Jaidi, J.; Dutta, P.: Modeling of transport phenomena in a gas metal arc welding process, Numer. heat transfer A 40, 543-562 (2001)
[27] Park, H.; Rhee, S.: Analysis of weld geometry considering the transferring droplets in gas metal arc welding, JSME int. J. ser. C 44, No. 3, 856-862 (2001)
[28] Davies, M. H.; Wahab, M.; Painter, M. J.: An investigation of the interaction of a molten droplet with a liquid weld pool surface: a computational and experimental approach, Weld. J. 79, No. 1, 18s-23s (2000)
[29] Arghode, V. K.; Kumar, A.; Sundarraj, S.; Dutta, P.: Computational modeling of GMAW process for joining dissimiliar aluminum alloys, Numer. heat transfer A 53, No. 4, 432-455 (2008)
[30] Hu, J.; Tsai, H. L.: Heat and mass transfer in gas metal arc welding. Part I. The arc, Int. J. Heat mass transfer 50, 833-846 (2007) · Zbl 1124.80329 · doi:10.1016/j.ijheatmasstransfer.2006.08.025
[31] Hu, J.; Tsai, H. L.: Heat and mass transfer in gas metal arc welding. Part II. The metal, Int. J. Heat mass transfer 50, 808-820 (2007) · Zbl 1124.80329 · doi:10.1016/j.ijheatmasstransfer.2006.08.025
[32] Hu, J.; Tsai, H. L.: Effects of current on droplet generation and arc plasma in gas metal arc welding, J. appl. Phys. 100, 053304 (2006)
[33] Hu, J.; Tsai, H. L.: Metal transfer and arc plasma in gas metal arc welding, ASME J. Heat transfer 129, 1025-1035 (2007) · Zbl 1124.80329
[34] D.B. Kothe, R.C. Mjolsness, M.D. Torrey, Ripple: A Computer Program for Incompressible Flows with Free Surfaces, LA-12007-MS, Los Alamos National Laboratory, 1991.
[35] Diao, Q. Z.; Tsai, H. L.: Modeling of solute redistribution in the mushy zone during solidification of aluminum – copper alloys, Metall. trans. A 24A, No. 4, 963-973 (1993)
[36] , Aluminum: properties and physical metallurgy, 13-19 (1984)
[37] Hu, J.; Guo, H.; Tsai, H. L.: Weld pool dynamics and the formation of ripples in 3D gas metal arc welding, Int. J. Heat mass transfer 51, 2537-2552 (2008) · Zbl 1144.80318 · doi:10.1016/j.ijheatmasstransfer.2007.07.042
[38] Zacharia, T.; David, S. A.; Vitek, J. M.: Effect of evaporation and temperature dependent material properties on weld pool development, Metall. trans. B 22B, No. 2, 233-241 (1992)
[39] Patankar, S. V.: Numerical heat transfer and fluid flow, (1980) · Zbl 0521.76003
[40] ASM, Properties and Selection: Nonferrous Alloys and Pure Metals, 9th ed, Metals Handbook, vol. 2, American Society for Metals, Metals Park, OH, 1985, p. 113.
[41] ASM, Metallography and Microstructures, 9th ed, Metals Handbook, vol. 9, American Society for Metals, Metals Park, OH, 1985, pp. 352 – 354.
[42] Kou, S.: Welding metallurgy, (1987)
[43] Enjo, T.; Kuroda, T.: Microstructure in weld heat-affected zone of al – mg – si alloy, Trans. JWRI 11, No. 1, 61-66 (1982)
[44] Malin, V.: Study of metallurgical phenomena in the HAZ of 6061-T6 aluminum welded joints, Weld. J. 74, No. 9, 305s-318s (1995)
[45] S.D. Dumolt, Metallurgical Transformations in the Heat-Affected Zone of Aluminum Alloys by Transmission Electron Microscopy, Carnegie-Mellon University, Pittsburgh, PA, 1983.
[46] Ceresara, S.; Di Russo, E.; Fiorini, P.; Giarda, A.: Effect of si excess on the aging behavior of al – mg2 – si 0.8% alloy, Mater. sci. Eng. 5, 220-227 (1969 – 1970)
[47] A.H. Maitland, A. Ried, Metallurgical events in the heat affected zone of AlMgSi alloys, in: International Aluminum Welding Conference, Cleveland, OH, 1981, pp. 106 – 114.
This reference list is based on information provided by the publisher or from digital mathematics libraries. Its items are heuristically matched to zbMATH identifiers and may contain data conversion errors. It attempts to reflect the references listed in the original paper as accurately as possible without claiming the completeness or perfect precision of the matching.